Synthesis and Flame Retardant Improvement of PU Coatings Containing Trichloro Modified Polyester/IPDI Isocyanurate

Two component polyurethane (PU) flame retardant coatings were prepared by blending trichloro modified polyesters (TCMPs) and isophorone diisocyanate isocyanurate. TCMPs were synthesized by polycondensation of trichlorobenzoic acid (TCBA), a flame retardant component, with adipic acid, 1,4 butanediol, and trimethylolpropane. The content of TCBA was varied in 10, 20, and 30 wt% for the reaction. Theses new flame retardant coatings showed various properties comparable to other non flame retardant coatings. Moreover, we carried out the combustion test and the flammability test for our flame retardant coatings. The results of vertical burning test for the coatings containing more than 20 wt% of TCBA were determined as no burn. The results of flammability test for the coatings with 20 wt% and 30 wt% of TCBA contents indicated the limiting oxygen index (LOI) values of 26% and 29% respectively, which implied relatively good flame retardancy.