Magnetite와 무기성 슬러지의 이산화탄소 분해 특성

Decomposition Characteristics of Carbon Dioxide Using Magnetite and Inorganic Sludge

Magnetite and inorganic sludge were mainly composed of Fe2O4 and Fe2O3, respectively. Initial specific surface areas of magnetite and inorganic sludge were 130 m2/g and 31.7 m2/g. CO2 decomposition rate for inorganic sludge was increased with temperature. Maximum CO2 decomposition rates were shown 89% for magnetite at 350℃ and 84% for inorganic sludge at 500℃. Specific surface area for magnetite was not varied significantly after CO2 decomposition. However, specific surface area for inorganic sludge was greatly decreased from initial 130 m2/g to approximately 50~60 m2/g after reaction. Therefore, it was estimated that magnetite could be used for CO2 decomposition for a long time and inorganic sludge should be wasted after CO2 decomposition reaction.