Evaluation of Physical Properties of Polyurethane Resin for Wound Covering according to PTMG, DMBA Application
- 한국응용과학기술학회 (구.한국유화학회)
- 한국응용과학기술학회지
- 한국응용과학기술학회지 제37권 제5호
-
2020.101248 - 1256 (9 pages)
-
DOI : 10.12925/jkocs.2020.37.5.1248
- 2
In this study, the polyurethane resin was synthesized by applying PTMG and DMBA of different composition ratios for the synthesis of water-dispersible polyurethane used in wound coating resin. The varying properties of the synthesized water-dispersible polyurethane were measured through tensile strength, elongation, and abrasion resistance analysis. As for the tensile strength measurement result according to the PTMG content, the sample with the highest reaction molar ratio was measured as 1.08 kgf/mm² and the elongation was measured as 520%. As for the tensile strength result according to the DMBA content, the sample with the highest reaction molar ratio was measured as 0.51 kgf/mm2, and the elongation was measured as 435%. The degree of surface destruction by the abrasion resistance measurement was visually confirmed through SEM.
1. Introduction
2. Experiment
3. Results and Discussion
4. Conclusion
References
(0)
(0)