Properties of Charcoal Board Manufactured from Domestic Wood Waste

This research was carried out to examine the properties of black charcoal board, in order to find the proper manufacturing condition for the black charcoal-board made of the charcoal. The charcoal in this study was distillated from domestic wood waste, and it were also the purpose of this study to see if the black charcoal-board has the advantageous properties of charcoal as a well-being building material against the sick house problem. Domestic wood waste was consisted of MDF 40%, PB 30%, plywood 15% and wood 15%, respectively. Black charcoal board was produced by hot pressing with following conditions; temperature 170℃, three stage pressing cycle of 40-10-40 kgf/ ㎠(1min.-2.5min.-5min.) and non formaldehyde adhesives〔P15%+M5%:MDI(M), poly vinyl acetate emulsion(P). Fine mixed particle size〔#6-12(16.9%), #12-18(16.7%), #12-40(47.2%), #40-60(9.5%), #60-100(5.9%), less than #100(3.8%)〕gave better results than larger particle size 〔 over #6(33.8%), #12-18(17.7%), #12-40(37.7%), #40-60(6.4%), #60-100(2.6%), less than #100(1.8%)〕. Final moisture content of the mat was best at 36%. Black charcoal-board showed less MOR and IB(internal bond), more WA(water absorption) than that of white charcoal-board. Black charcoal board showed not only the same gas adsorption and dimensional stability as white charcoal board but also good cutting, nailing and drilling for indoor environment systems.

Ⅰ. INTRODUCTION

Ⅱ. EXPERIMENT

CONCLUSION

REFERENCES

로딩중