납과 텅스텐 기반 차폐체의 성능 비교 평가

Evaluation of the Shield Performance of Lead and Tungsten Based Radiation Shields

This study was intended to evaluate the shielding rate of radiation shields manufactured using 3D printers that have recently been used in various fields by comparing them with existing shields made of lead, and to find out their applicability through experiments. A 3D printer shield made of tungsten filament 1 mm, 2 mm, 4 mm shield, RNS-TX (nanotungsten) 1.1 mm, lead 0.2 mmPb, and 1mmPb were exposed to 99mTc, 18F, and 201TI for 15, 30, 45 minutes, and 60 minutes after measuring cumulative dose three times. Based on this, the shielding rate of each shield was calculated based on the dose in the absence of the shield. In addition, 99mTc, 18F, and 201TI were located 100 cm away from the phantom in which the OSLD nano Dot device was inserted, and if there was no shield for 60 minutes, the dose of thyroid was measured using 1.0 mm of lead shield, 1.1 mm of RNS-TX shield, and 2 mm of tungsten shield made by 3D printer. The use of shields during radiation shielding emitted from open radiation sources all resulted in a reduction in dose. The radiation dose emitted from the radionuclides under the experiment was all reduced when the shield was used. This study has been confirmed that tungsten is a material that can replace lead due to its excellent performance and efficiency as shield, and that it even shows the possibility of manufacturing a customized shield using 3D printer.