반도체 몰딩 공정에서 발생하는 EMC 폐기물의 재활용을 통한 실리카 나노입자의 제조 및 반도체용 CMP 슬러리로의 응용

In this study, EMC(Epoxy molding compound) waste from the semiconductor molding process is recycled and synthesized into silica nanoparticles, which are then applied as abrasive materials contains CMP(Chemical mechanical polishing) slurry. Specifically, silanol precursor is extracted from EMC waste according to the ultra-sonication method, which provides heat and energy, using ammonia solution as an etchant. By employing as-extracted silanol via a facile sol-gel process, uniform silica nanoparticles(e-SiO2, experimentally synthesized SiO2) with a size of ca. 100nm are successfully synthesized. Through physical and chemical analysis, it was confirmed that e-SiO2 has similar properties compared to commercially available SiO2(c-SiO2, commercially SiO2). For practical CMP applications, CMP slurry is prepared using e-SiO2 as an abrasive and tested by polishing a semiconductor chip. As a result, the scratches that are roughly on the surface of the chip are successfully removed and turned into a smooth surface. Hence, the results present a recycling method of EMC waste into silica nanoparticles and the application to high-quality CMP slurry for the polishing process in semiconductor packaging.

본 연구에서는 반도체 패키징의 몰딩 공정에서 발생하는 EMC 폐기물을 재활용하여 실리카 나노입자를 성공적으로 제조하였으며, 이를 CMP 공정용 슬러리의 연마재 물질로 응용하였다. 상세히는, EMC 폐기물을 암모니아 용액과 소니케이터를 활용하여 열과 에너지를 가하는 에칭 과정을 통해 실리카 나노입자를 제조하기 위한 실라놀 전구체를 추출하였다. 이후 실라놀 전구체를 활용하여 졸-겔법을 통해 약 100nm를 나타내는 균일한 구형의 실리카 나노입자(e-SiO2, experimentally synthesized SiO2)를 합성하였다. 제조한 e-SiO2는 물리화학적 분석을 통해 상용화된 실리카 입자(c-SiO2, commercially SiO2)와 동일한 형상과 구조를 지니고 있음을 확인할 수 있었다. 최종적으로, e-SiO2를 연마재로 사용하여 CMP 공정용 슬러리를 제조하여 실제적인 반도체 칩의 연마 성능을 확인하였다. 그 결과, 반도체 칩의 표면에 존재하던 스크래치가 성공적으로 제거되어 매끈한 표면으로 바뀌게 된 것을 확인하였다. 본 연구 결과는 물질의 재활용법에 대한 설계를 통해 EMC 폐기물의 부가가치를 향상시키기 위하여 반도체 공정에서 대표적으로 활용되는 고부가가치 소재인 실리카 입자로 성공적으로 제조하고 이를 응용하는 방법에 대해 제시하였다.

로딩중