Two Crystal structures of Fully Dehydrated Partially Magnesium Exchanged Zeolite A, $Mg_{1.5}Na_9-A\;and\;Mg{2.5}Na_7$-A

Two Crystal structures of fully dehydrated partially magnesium exchanged zeolite A, stoichiometries of $Mg_{2.5}Na_7-A$ (a = 12.251 (1) ${\AA}$) and $Mg_{1.5}Na_9-A\; (a\;=\;12.214(1)\;{\AA})$ per unit cell, have been determined from the 3-dimensional X-ray diffraction data gathered by counter methods. All structures were solved and refined in the cubic space group Pm3m at 21(1)$^{\circ}C$. The structures of the dehydrated $Mg_{2.5}Na_7-A$ and $Mg_{1.5}Na_9-A$ were refined to yield the final error indices $R_1$ = 0.042 and $R_2$ = 0.049 with 318 reflections, and $R_1$ = 0.034 and $R_2$ = 0.032 with 252 reflections, respectively, for which I > $3{\sigma}(I)$. Both structures indicate that $Mg^{2+}$ ions are coordinated by three framework oxygens and the angle substended at $Mg^{2+}$ ions, O(3)-Mg(1)-O(3) is ca. $120^{\circ}$, close to the idealized trigonal planar value. $Mg^{2+}$ ions preferentially occupy 6-ring sites and $Na^+$ ions occupy 8-ring sites when total number of cations per unit cell is more than 8.