Black Chrome 태양광 선택흡수막의 표면분석

Surface Analysis of Black Chrome Solar Selective Coatings

The thermal degradation of electroplated black chrome coating on Ni substrates has been investigated by using Auger electron spectroscopy technique. The sample was prepared by electroplating at $20^{\circ}C$ for 20 seconds with the current density at $0.4A/cm^2$. Its surface oxidation process was investigated with 1 hour annealed sample for a temperature range of $300-550^{\circ}C$. While its optical solar absorption was dominated by fine metallic Cr particles, thermal degradation was occurred primarily by oxidation of metallic Cr particles as increasing the annealing temperature.