글라스아이오노머 시멘트 표면 처리에 따른 치과용 아말감의 전단 결합 강도에 관한 연구

A STUDY ON BONDING STRENGTH OF DENTAL AMALGAM TO GLASS IONOMER CEMENT FOLLOWING SURFACE TREATMENT

The purpose of this study was to assess the 24-hour shear bond strength of amalgam to glass ionomer cement, using five different intermediaries. The intermediaries used in this study were Scotchbond 2 (light curing dentin adhesive), Panavia (resin cement), liquid' of glass ionomer cement (chemical curing & light curing), and uncured mixture of light curing glass ionomer cement. This study was operated with 48 specimens devided into 6 groups. The experimental groups are as follows: Group 1 : Bonded Amalgam to chemical curing glass ionomer cement with liquid of chemical curing glass ionomer. Group 2 : Bonded Amalgam to light curing glass ionomer cement with liquid of chemical curing glass ionomer. Group 3: Bonded Amalgam to light curing glass ionomer cement with resin cement. Group 4: Bonded Amalgam to light curing glass ionomer cement with light curing dentin adhesive. Group 5: Bonded Amdlgam to light curing glass ionomer cement with liquid of light curing glass ionomer. Group 6: Bonded Amalgam to light curing glass ionomer cement with uncured mixture of light curing glass ionomer cement. 30 minutes after amalgam condensation, all specimens were stored for 24 hours in water at $37^{\circ}C$ and tested with Instron (1122). The following results obtained: 1. The shear bond strength of group 6 was higher than those of the other groups (46.7 kgf/$cm^2$, p<0.05). 2. The shear bond strength of resin cement intermediary group was lower than that of the group using uncured mixture of light curing glass ionomer cement. 3. The results of group 1 and group 2 were different, even though the inter-me diaries used were same. 4. Intermediary of Group 5 did not show complete set in Scanning Electromicroscopic examination. 5. Light-curing dentin adhesive did not show any bonding ability to amalgam.