핵폐기용 모의글라스의 조성변화에 따른 용출특성에 관한 연구

Study on the Leaching Characteristics of Simulated Nuclear Waste Glass with variable Composition

In order to manufacture an attractive waste glass for the permanent and secure disposal of high-level radioactive waste, the complex composition of the simulated nuclear waste glass PNL-7668 was simplified to a composition of sodium borosilicate glass. The substitutions of $Fe_2O_3$ and $Al_2O_3$ were added to examine on the leaching characteristics of simulated nuclear waste glass with variable composition. The leach tests for these glasses were performed according to 'MCC-1, Static Leach Test Procedure' in acid and basic solution. In this study, for the $Al_2O_3$-containing glasses, Na ion release from these glasses was higher in acid solution than in basic solution. As the content of $Fe_2O_3$ was increased in glasses, Na ion release was increased in acid solution, in spite of decrease of amount of total mass diminution.