EFFECTS OF NITROGEN AND CARBON ION IMPLANTATION INTO AUSTENITIC STAINLESS STEEL ON HYDROGEN ABSORPTION

EFFECTS OF NITROGEN AND CARBON ION IMPLANTATION INTO AUSTENITIC STAINLESS STEEL ON HYDROGEN ABSORPTION

The effect of implanted nitrogen and carbon ion into SUS 304 on the absorption of hydrogen by cathodic chaging were studied. Implantations of $N^+$, $C^+$ were performed with doses of $3\times10^{17}$ ions $\textrm{cm}^2$ and $5\times10^{17}N^+cm^2$, and $5\times10^{17}C^+cm^2$, at an energy of 90 keV. Nitrides and carbide were investigatedby X-ray diffraction, Auger electron spectroscopy (AES) and scanning electron microscope (SEM). Formation of hydrides during cathodic charging were depressed by a modified surface layer. It is concluded that the both nitrides and carbides act as the barrier of hydrogen migration and the catalyst of desorption of cathodically charged hydrogen.