TSSG-pulling of sillenite $Bi_{12}TiO_{20}$ for EOS application

TSSG-pulling of sillenite $Bi_{12}TiO_{20}$ for EOS application

The reproducibility of successive growth of $Bi_{12}TiO_{20}$ (BTO) single crystlas using a top-seeded solution growth (TSSG) pulling method was evalutated by measuring the lattice constants and their standard deviations. A substantial phase diagram in the region close to the stoichiometric BTO was established expermentally for this purpose, and the existence of a retrograde solid solution close to a BTO was clarified. It was emphasized that a starting solution, with a 10.0~10.1 mol% $TiO_{2}$ concentration, results in large single crystals with a highly homogeneous lattice constant of within ${\pm}1{\times}10^{-4}\AA$, when the solidified fraction of the grown crystal is less than about 45 %. A wavelength dispersion of refractive index was measrued for the first time, and it was verified that the refractive index of BTO is larger than that of BSO($Bi_{12}TiO_{20}$), allowing the voltage sensitivity of EOS higher than the case with BSO as a probe head.