극초단파의 출력과 적용시간이 의치상용 레진의 물리적 성질에 미치는 영향

THE INFLUENCE OF WATTAGE AND CURING TIME OF MICROWAVE ENERGY ON PHYSICAL PROPERTIES OF THE DENTURE BASE RESIN

The purpose of this study was to evaluate the effect of wattage and curing time on surface hard-ness, three-point bending strength and internal porosity of microwave curing denture base resin. Two sizes of resin specimens were made of Acron $MC^{(R)}\;;\;3.5{\times}10{\times}60mm$ for surface hardness and three-point bending strength measurement and $5{\times}12{\times}60mm$ for internal porosity measurement. They were cured by microwave energy at varing wattages(500W, 700W) and curing times(2min., 3min., 4min.) to determine if a certain wattage/curing time combination would improve physical properties. Surface hardness was measured with Vikers hardness tester, three-point bend-ing strength with universal testing machine and internal porosity was calculated by measuring the weight in air and in water. The results obtained were as follows: 1. There was no significant difference in percent porosity among experimental groups(p>0.05). 2. 500W/3min. group showed the higher surface hardness than 700W/2, 3, 4min. groups(p<0.05), and 700W/4 min. group showed the lower surface hardness than 500W/2, 3, 4min. groups(p<0.05), but there was no significant difference among others(p>0.05). 3. 500W/3min. group yielded the higher value of bending strength than 500W/2min., 700W/3, 4min. groups(p<0.05), but there was no significant difference among others(p>0.05).