초음파 분무 열분해법으로 제조한 ZnO막의 전기적, 구조적 특성에 미치는 인듐 확산 효과

Indium Diffusion Effects on the Structural and Electrical Properties of ZnO Films Prepared by Ultrasonic Spray Pyrolysis

Zinc oxide (ZnO) films deposited on indium (In) films were post-annealed in a rapid thermal anealing (RTA) system. The ZnO/In films were RTA-treated in air or a vacuum ambient. The crystallographic properties and surface morphologies of the films were studied before and after the RTA by X-ray diffraction(XRD) and scanning electron microscopy (SEM), respectively. The resistivity variation of the films with RTA temperature and time was measured by the 4-point probe method. Auger electron spectroscopy (AES) was carried out to figure out the redistribution of indium atoms in the ZnO films. The resistivity of the ZnO/In films decreased to 2$\times$10$\^$-3/ Ωcm by diffusion of the In. The In diffusion into the ZnO films roughened the surface of ZnO films. The results of depth profile by AES showed a hump of In atoms around ZnO/In interface after the RTA at 800 $\^{C}$. The effects of temperature time and ambient during the RTA on the structural and electrical properties of the ZnO/In films were discussed.