Study on Sol-Gel Prepared Phosphosilicate Glass-Ceramic For Low Temperature Phosphorus Diffusion into Silicon

Study on Sol-Gel Prepared Phosphosilicate Glass-Ceramic For Low Temperature Phosphorus Diffusion into Silicon

A new solid source for low temperature diffusion into silicon was developed. The source wafer consists of an “active” compound, which is sol-gel prepared phosphosilicate glass-ceramics containing 56% P$_2$O$\sub$5/, embedded in a skeletal foam-like, inert substrate. Phosphorus diffusion from the new solid sources at low temperatures (800-875$^{\circ}C$) produced reprodecible sheet resistances and shallow junctions. From a series of one hour doping runs, the life time of the phosphosilicate source was determined to be over 40 hours. The effective diffusion coefficient of phosphorus into silicon and the corresponding activation energy at 850$^{\circ}C$ were determined to be 7.5${\times}$10$\^$-15/ $\textrm{cm}^2$/sec and ∼3.9 eV, respectively.