Dielectric Properties of Zr-doped (Ba,Sr,Ca)TiO₃ Thick Films for Microwave Phase Shifters

Dielectric Properties of Zr-doped (Ba,Sr,Ca)TiO₃ Thick Films for Microwave Phase Shifters

(Ba,Sr,Ca)TiO$_3$ powders, prepared by the sol-gel method, were mixed with organic binder and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. All the BSCT thick films, sintered at 1420$^{\circ}C$, showed the typical XRD patterns of a perovskite polycrystalline structure. The average grain sizes decreased with increasing amounts of ZrO$_2$, and the BSCT(40/40/20) thick films doped with 2wt% MnO$_2$ showed a value of 8$\mu\textrm{m}$. The thickness of thick films by four-cycle on printing/drying was approximately 951$\mu\textrm{m}$. The relative dielectric constant decreased with increasing Ca content and MnO$_2$ doping amount. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) thick films doped with 2.0wt% ZrO$_2$ were 772, 0.184％ and 15.62%, respectively.