FBAR 소자제작을 위한 ZnO 박막 증착 및 특성

Characteristics of ZnO Thin Film for SMR-typed FBAR Fabrication

This paper gives characterization of ZnO thin film deposited by RF magnetron sputtering method, which is concerned in deposition process and device fabrication process, to fabricate solidly mounted resonator(SMR)-type film bulk acoustic resonator(FBAR). A piezoelectric layer of 1.1${\mu}{\textrm}{m}$ thick ZnO thin films were grown on thermally oxidized SiO$_2$(3000 $\AA$)/Si substrate layers by RF magnetron sputtering at the room temperature. The highly c-axis oriented ZnO thin film was obtained at the conditions of 265 W of RF power, 10 mtorr of working pressure, and 50/50 of Ar/O$_2$ gas ratio. The piezoelectric-active area was 50 ${\mu}{\textrm}{m}$${\times}$50${\mu}{\textrm}{m}$, and the thickness of ZnO film and Al-3 % Cu electrode were 1.4 ${\mu}{\textrm}{m}$ and 180${\mu}{\textrm}{m}$, respectively. Its series and parallel frequencies appeared at 2.128 and 2.151 GHz, respectively, and the qualify factor of the resonator was as high as 401.8$\pm$8.5.