0.01d 폴리에스테르 초극세 섬유의 염색성 및 역학적 성질

Dyeing and Mechanical Properties of 0.01d Polyester Ultramicro Fiber

In this article, effect of the dyeing and mechanical properties were investigated on the polyester ultramicro fiber(UMF) and knitted fabric varying fiber fineness(0.01d and 0.05d). By a treatment with NaOH solution, sea-ingredient was removed and polyester micro-fiber was revealed. The dyeing, build-up and fastness properties of the fiber and fabrics were observed. We used C.I. Disperse Red 60 and Blue 56 for dyeing property and eight Lumacron dyes for build-up property and colorfastness. At low temperature dyeing($100^{\circ}C$), the dyeing rate of 0.01d-polyester UME increased more than that of 0.05d-polyester UMF with Disperse Red 60 and Blue 56 whereas dyeing rate of 0.05d-polyester UMF were increased more than that of 0.01d-polyester UMF at high temperature($120^{\circ}C$), The colorfastnesses of the 0.05d-fiber knitted fabric such as washing, rubbing and light was higher than those of the 0.01d-fiber knitted fabric.