AZ31 마그네슘 합금의 플라즈마전해산화 피막 형성에 미치는 수산화 이온 및 규산 이온의 영향

Effects of Hydroxide and Silicate ions on the Plasma Electrolytic Oxidation of AZ31 Mg Alloy

Formation behavior of PEO (Plasma Electrolytic Oxidation) films on AZ31 Mg alloy was studied in aqueous solutions containing various concentrations of hydroxide ion ($OH^-$) and silicate ion ($SiO_3{^{2-}}$) by voltage-time curves, and corrosion resistance of the PEO film-covered specimen was investigated by immersion test in 0.5 M NaCl solution. From the analyses of the voltage-time curves, it is suggested that two different types of anions are essentially needed for the formation of PEO films on AZ31 Mg alloy: film formation agent and local film breakdown agent. $SiO_3{^{2-}}$ ion acts only as a film formation agent but $OH^-$ ion acts not only as a film formation agent but also film breakdown agent. The PEO films prepared on AZ31 Mg alloy in alkaline silicate solution showed very good corrosion resistance without any pitting or filiform corrosions up to 480 h of immersion in 0.5 M NaCl.