Synthesis and Characterization of Cu²⁺-Perfluorophthalocyanine Incorporated SBA15

After anchoring 3-(2-aminoethylamino)propyltriethoxysilane (APTES) onto the surfaces of the channels within ordered mesoporous silica, SBA-15, we dispersed $Cu^{2+}$-perfluorophthalocyanine into the modified SBA-15 channels. From small-angle X-ray scattering (SAXS) patterns and transmission electron microscopy (TEM) images, we confirmed that both the calcined and $Cu^{2+}$-perfluorophthalocyanine-incorporated SBA-15 samples possessed ordered periodic structures and hexagonal symmetry lattices (p6mm). The value of the $d_{100}$ spacing was decreased after the incorporation of $Cu^{2+}$-perfluorophthalocyanine into the modified SBA-15 channels. We used FTIR and UV-Vis spectroscopy and thermogravimetric analysis (TGA) to characterize both the modified SBA-15 and the $Cu^{2+}$-perfluorophthalocyanine-incorporated SBA-15 samples. From scanning electron microscopy (SEM) images and $N_2$ sorption measurements, we found that the $Cu^{2+}$-perfluorophthalocyanine units were incorporated within the modified SBA-15 channels, rather than on the external surfaces of the modified SBA-15 channels.