저탄소강의 크롬도금층 형성 및 내식성에 미치는 Na₂MoO₄ 첨가의 영향

The effect of Na₂MoO₄ addition on the formation and corrosion resistance of Cr-electroplated layer of low carbon steel

Presence of cracks in electrodeposited hard chromium layer, which provide a path of corrosive media to steel substrate, is a serious issue in metal finishing with chromium electroplating. In this study, we added sodium molybdate in an electrolyte for chromium electroplating bath. 130g/L of sodium molybdate in Sargent bath for chromium electroplating causes a codepostion of molybdenum with chromium in a rage of 0.61 ~ 3.14 wt.%. The co-deposited molybdenum enhances the crystallinity of chromium layer, thus the hardness is slightly decreases by the addition of molybdate in electrolyte. However, due to the co-deposition of molybdenum, a crack-free chromium layer could be electrodeposited. Such crack-free chromium layer shows a significantly improved corrosion resistance.