Effect of the sintering technology on the properties of fired brick from quartz sands

Effect of the sintering technology on the properties of fired brick from quartz sands

River sands as low grade natural raw materials are used to prepare the fired brick to replace clay fired bricks, which aims to save land resources and use low grade natural resources to realize high cost performance. In this paper, the effect of sintering technology of bricks on their performance is discussed. The compressive strength of fired bricks is first increased and then decreased with an increase in the sintering temperature, the compressive strength of bricks prepared by the isostatic compaction shaping is higher than that of bricks prepared by the plastic shaping under the same conditions. The compressive strength of bricks reaches 28 MPa when sintered at 1150 oC by using a 20MPa isostatic compaction shaping method. The compressive strength of bricks is first increased and then decreased by prolonging the holding time, the compressive strength of bricks reaches 28.9MPa when sintered at 1150 oC for 2 h.

River sands as low grade natural raw materials are used to prepare the fired brick to replace clay fired bricks, which aims to save land resources and use low grade natural resources to realize high cost performance. In this paper, the effect of sintering technology of bricks on their performance is discussed. The compressive strength of fired bricks is first increased and then decreased with an increase in the sintering temperature, the compressive strength of bricks prepared by the isostatic compaction shaping is higher than that of bricks prepared by the plastic shaping under the same conditions. The compressive strength of bricks reaches 28 MPa when sintered at 1150 oC by using a 20MPa isostatic compaction shaping method. The compressive strength of bricks is first increased and then decreased by prolonging the holding time, the compressive strength of bricks reaches 28.9MPa when sintered at 1150 oC for 2 h.