The purpose of this study was to evaluate the elastic memory process in cold worked stainless steel wire and the effect of heat treatment on it. 0.018 inch round and 0.019 X 0.025 inch rectangular wire (ORMCO stainless wire) were used in this study. Each wire type had 4 groups: non-heat treatment group, furnace heat treatment group, electric current heat treatment group, and bending after heat treatment group. Each group was consisted of 10 specimens. With the Jig, each wire was bent into v-shape uniformly, and width of two free ends of each v-shaped wire was measured by caliper (to the point of 0.1mm correctly) at time interval of off-jig, after heat treatment, 1, 2, 3. 4 hours, I, 2, 3,4, 5, 6 days, 1, 2, 3, 4 weeks after. The results were as follows: 1. In non-heat treatment group and bending after heat treatment group, elastic memory process was occured 60% within 1 hour, and more than 90% within 1 week. 2. In furnace and electric current heat treatment group, almost all elastic memory process was occured during heat treatment, and then specimen was stabilized dimensionally. 3. Magnitude of deformation by elastic memory was greater in heat treatment group than non heat treatment group and bending after heat treatment group. 4. There was no remarkable difference in deformation pattern between 0.018 inch round wire and 0.019 x 0.025 inch rectangular wire.